C26000 Cartridge Brass
分类: Metal Materials
标准: ASTM B36, JIS C2600, GB H68
密度: 8.53 g/cm³
基本信息
- 材料类型
- Brass (Copper Alloy)
- CNC加工特性
- 优秀
- 3/5轴适应性
- 适合
- 变形风险
- 低
- 粘刀性
- 否
- 切削液推荐
- Water-soluble coolant (5-8% emulsion) for general machining; compressed air for dry cutting. High pressure coolant (20-40 bar) for deep hole drilling.
加工要点：C26000黄铜切削力小，切屑呈短碎状，表面光洁度好。使用锋利刀具避免加工硬化，断屑槽设计有助于排屑。建议恒温切削减少热变形。
化学成分
| 元素 | 含量 |
|---|---|
| Cu | 68.5 – 71.5% |
| Zn | Remainder |
| Pb | ≤ 0.07% |
| Fe | ≤ 0.05% |
物理性能
- 硬度
- 100 HRB (typical, 1/4 hard)
- 热导率
- 120 W/m·K (at 20°C)
- 比热容
- 377 J/kg·K
- 热膨胀系数
- 19.9 ×10⁻⁶/°C (20-300°C)
- 熔点
- 920 – 935°C
力学性能
- 抗拉强度
- 370 – 450 MPa (1/4 hard)
- 屈服强度
- 250 – 350 MPa (0.2% offset, 1/4 hard)
- 延伸率
- 30 – 45% (in 50 mm)
- 断面收缩率
- 45 – 60%
- 冲击韧性
- 14 – 18 J/cm² (Izod)
刀具推荐
- 车削
- Carbide inserts (ISO K10-K20) with sharp edge, positive rake. Uncoated or TiN-coated.
- 铣削
- Carbide end mills (uncoated or AlTiN) for high-speed finishing; HSS for roughing with large DOC.
- 钻孔
- HSS twist drill with 118° point angle or carbide drill for production. Peck cycle recommended for deep holes.
切削参数
车削
速度: 200 – 400 m/min | 进给: 0.10 – 0.30 mm/rev | 深度: 1.0 – 4.0 mm
铣削
速度: 250 – 500 m/min | 进给: 0.08 – 0.25 mm/tooth | 深度: 1.0 – 3.0 mm
钻孔
速度: 60 – 120 m/min (HSS), 120 – 200 m/min (Carbide) | 进给: 0.05 – 0.20 mm/rev | 深度: 0.5 – 2.0 mm (per pass for peck drilling)
攻丝
速度: 10 – 25 m/min (HSS tap) | 丝锥规格: M4 – M16 (coarse thread preferred)
热处理
- Annealing: 550-650°C for stress relief and softening
- Stress relief: 250-350°C for 1-2 hours to reduce residual stress
表面处理
- Electroplating (Ni, Zn, Sn, Cr)
- Passivation (chromate or non-chromate)
- Polishing and buffing for high gloss
- Lacquer coating for tarnish protection
材料特性
- Excellent machinability with low tool wear
- Good corrosion resistance in atmospheric and aqueous environments
- High ductility and formability for cold working operations
- Non-magnetic and good electrical/thermal conductivity
适用场景
- Ammunition casings and components
- Electrical connectors, terminals, and fuse clips
- Automotive radiator fins and heat exchanger tubes
不适用场景
- High-temperature structural parts (above 300°C)
- Wear-resistant sliding components without lubrication
常见问题
C26000黄铜的切削速度范围是多少？
车削推荐200-400 m/min，铣削推荐250-500 m/min，钻削HSS刀具60-120 m/min，硬质合金120-200 m/min。具体速度取决于刀具涂层、冷却条件和所需表面质量。
C26000在CNC加工中容易出现哪些问题？
主要问题包括：长切屑缠绕（可通过断屑槽解决）、加工表面粗糙度过粗（需提高转速或降低进给）、薄壁件变形（需减小径向切削力）。一般不出现粘刀或积屑瘤。
加工C26000黄铜时是否需要冷却液？
推荐使用水溶性乳化液（5-8%浓度）进行冷却和润滑，可提高表面光洁度并延长刀具寿命。干切削也可行，但需使用压缩空气排屑。深孔加工时建议使用高压冷却液。
C26000黄铜的三轴和五轴加工适应性如何？
C26000非常适合三轴和五轴加工。其低切削力和短切屑特性使得复杂曲面和深腔加工流畅进行。五轴加工时需注意薄壁部位支撑，避免振动。
C26000与国标H68黄铜是否等效？
是的，C26000（UNS）对应国标H68（GB/T 5231），成分均为Cu 68-71%，余量Zn。两者在物理力学性能和加工特性上基本一致，可互换使用。